It is well known that cryogenic treatment is used to improve the mechanical properties of a material. Consequently, the use of cryogenic treatment has grown beyond its successful application on tool steels. In this research, the effects of cryogenic treatment on the corrosion of AISI D3 steel in 3.5% NaCl solution were examined by electrochemical impedance spectroscopy (EIS). The surface structure of the AISI D3 steel was examined by scanning electron microscopy (SEM) after the EIS investigations. Results clearly indicated that the pre-treatment of the steel was responsible for a significant effect on corrosion. The heat treatment process prior to the cryogenic treatment and the tempering process after were shown to decrease corrosion resistance.

The inhibition effect of mad honey on corrosion of 2007-type aluminium alloy in 3.5% NaCl solution was investigated by Tafel extrapolarisation (TP), electrochemical impedance spectroscopy (EIS) and dynamic electrochemical impedance spectroscopy (DEIS). All the studied parameters exhibited good anti-corrosive properties against corrosion of 2007-type aluminium alloy in the test solution; the corrosion rates decreased with the increase of the mad honey concentration. The surface morphology of the alloy was examined under scanning electron microscopy (SEM) in the absence and presence of the inhibitor. The inhibitory adsorption processes of mad honey on the 2007-type aluminium alloy surfaces conformed to the Langmuir adsorption isotherm.